Mupeak RP Calipers
The Mupeak RP series is ideal for those who prioritize track driving, time attack, or club racing, while also allowing for street use.
RP-7
Specifications:
Caliper code: RP7
Structure & Materials: 2 piece 6082 Fully Forged Aluminum Alloy,
Weight: 4.3KG / 9.4LBS
Brake Pad Thickness: 25mm
Piston Materials : Stainless Steel
Anti Knock Back Spring : Yes
Piston coatings : Yes / Titanium Nitride (Tin) Coated
Piston Heat Treatment: Yes
Piston Number: 6
Piston Spec : 27mm, 31,8mm, 38mm / 1.063'', 1.252'', 1.496'' (*diameter varies depends on the applications )
Pistons Surface Area : 50cm² / 7.75 Square inch
Minimum Brake Rotor Diameter : 355mm
Manufactural tech and test info
Tensile Strength: 320Mpa
Caliper Housing Hardness: HV400
Low Pressure Sealing Test: The caliper passes a 0.4 MPa air pressure test, with a stabilization period of 5 seconds, and a pressure drop not exceeding 100 Pa.
High Pressure Sealing Test: The caliper passes a 12 MPa air pressure test, with a stabilization period of 5 seconds, and a pressure drop not exceeding 0.2 MPa.
Ultra-High Pressure Test: A sample of calipers passes a 30 MPa oil pressure test without failure or bursting.
Testing Standards: ISO 3996/ SAE J1603/ ECE R13/ QCT592
RP-6
Specifications:
Caliper code: RP6
Structure & Materials: 2 piece 6082 Fully Forged Aluminum Alloy,
Weight: 3.1KG / 6.8LBS
Brake pads Thickness: 18mm - D54
Anti Knock Back Spring : Yes
Piston Materials : Stainless Steel
Piston coatings : Yes / Titanium Nitride (Tin) Coated
Piston Heat Treatment: Yes
Piston Number: 6
Piston Spec : 27mm, 31,8mm, 38mm / 1.063'', 1.252'', 1.496'' (*diameter varies depends on the applications )
Pistons Surface Area : 50cm² / 7.75 Square inch
Minimum Brake Rotor Diameter : 355mm
Manufactural tech and test info
Tensile Strength: 320Mpa
Caliper Housing Hardness: HV400
Low Pressure Sealing Test: The caliper passes a 0.4 MPa air pressure test, with a stabilization period of 5 seconds, and a pressure drop not exceeding 100 Pa.
High Pressure Sealing Test: The caliper passes a 12 MPa air pressure test, with a stabilization period of 5 seconds, and a pressure drop not exceeding 0.2 MPa.
Ultra-High Pressure Test: A sample of calipers passes a 30 MPa oil pressure test without failure or bursting.
Testing Standards: ISO 3996/ SAE J1603/ ECE R13/ QCT592
Mupeak SP Calipers
The Mupeak SP series is designed for not only for big brake aesthetic but also ready for high-performance sprint driving on the street, as well as occasional track or High-Performance Driver Education (HPDE) driving.
Specifications:
Caliper code: SP4
Structure & Materials: 2 piece 6061-T6 Fully Forged Aluminum Alloy,
Weight: 2.9KG / 6.3LBS
Brake pads Thickness: 16.5mm- D48(F50)
Piston Materials : Aluminum
Piston coatings : Yes / Titanium Nitride (Tin) Coated
Piston Heat Treatment: Yes
Piston Number: 4
Piston Spec : ,31,8mm x 4 (*diameter varies depends on the applications )
Pistons Surface Area : 45.3cm² / 7.02 Square inch
Minimum Brake Rotor Diameter : 295mm
Manufactural tech and test info
Tensile Strength: 320Mpa
Caliper Housing Hardness: HV400
Low Pressure Sealing Test: The caliper passes a 0.4 MPa air pressure test, with a stabilization period of 5 seconds, and a pressure drop not exceeding 100 Pa.
High Pressure Sealing Test: The caliper passes a 12 MPa air pressure test, with a stabilization period of 5 seconds, and a pressure drop not exceeding 0.2 MPa.
Ultra-High Pressure Test: A sample of calipers passes a 30 MPa oil pressure test without failure or bursting.
Testing Standards: ISO 3996/ SAE J1603/ ECE R13/ QCT592